Investigation of the resistance behavior of LaMnO3/Bi4Ti3O12/Ba0.4Sr0.6TiO3/MgO film heterostructures

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Рұқсат ақылы немесе тек жазылушылар үшін

Аннотация

The temperature behavior of the LaMnO3/Bi4Ti3O12/Ba0.4Sr0.6TiO3/MgO heterostructure resistance was studied. Within the temperature range of 120–180 K, an anomalous region with two resistance maxima was found. Below 120 K, a transition to a metallic character of conductivity occurs. It was revealed the significant increase of the heterostructure resistance under the influence the green light radiation.

Авторлар туралы

D. Pavlov

Zаvоisky Physiсаl-Teсhniсаl Institute, Federal Research Centre Kаzаn Sсientifiс Сentre оf the Russian Acdemy of Sciences

Хат алмасуға жауапты Автор.
Email: dmitry.p.pavlov@mail.ru
Russiа, 420029, Kаzаn

A. Chibirev

Zаvоisky Physiсаl-Teсhniсаl Institute, Federal Research Centre Kаzаn Sсientifiс Сentre оf the Russian Acdemy of Sciences

Email: dmitry.p.pavlov@mail.ru
Russiа, 420029, Kаzаn

T. Salikhov

Zаvоisky Physiсаl-Teсhniсаl Institute, Federal Research Centre Kаzаn Sсientifiс Сentre оf the Russian Acdemy of Sciences

Email: dmitry.p.pavlov@mail.ru
Russiа, 420029, Kаzаn

R. Mamin

Zаvоisky Physiсаl-Teсhniсаl Institute, Federal Research Centre Kаzаn Sсientifiс Сentre оf the Russian Acdemy of Sciences

Email: dmitry.p.pavlov@mail.ru
Russiа, 420029, Kаzаn

Әдебиет тізімі

  1. Hossain M.K., Hossain S., Ahmed M.H. et al. // ACS Appl. Electron. Mater. 2021. V. 3. P. 3715.
  2. Thiel C.W., Macfarlane R.M., Sun Y. et al. // Laser Phys. 2014. V. 24. Art. No. 106002.
  3. Hossain M.K., Ahmed M.H., Khan I. et al. // ACS Appl. Electron. Mater. 2021. V. 3. P. 4255.
  4. Hossain M.K., Raihan G.A., Akbar A. et al. // ACS Appl. Electron. Mater. 2022. V. 4. P. 3327.
  5. Ohtomo A., Hwang H.Y. // Nature. 2004. V. 427. P. 423.
  6. Thiel S., Hammerl G., Schmehl A. et al. // Science. 2006. V. 313. P. 1942.
  7. Reyren N., Thiel S., Caviglia A.D. et al. // Science. 2007. V. 317. P. 1196.
  8. Li D., Gariglio S., Cancellieri C. et al. // APL Mater. 2014. V. 2. Art. No. 012102.
  9. Pavlenko N., Kopp T., Tsymbal E. et al. // Phys. Rev. B. 2012. V. 86. Art. No. 064431.
  10. Pavlenko N., Kopp T., Tsymbal E. et al. // Phys. Rev. B. 2012. V. 85. Art. No. 020407.
  11. Pavlenko N., Kopp T., Mannhart J. et al. // Phys. Rev. B. 2013. V. 88. Art. No. 201104.
  12. Lechermann F., Boehnke L., Grieger D. et al. // Phys. Rev. B. 2014. V. 90. Art. No. 085125.
  13. Salluzzo M., Gariglio S., Stornaiuolo D. et al. // Phys. Rev. Lett. 2013. V. 111. Art. No. 087204.
  14. Pavlov D.P., Zagidullin R.R., Mukhortov V.M. et al. // Phys. Rev. Lett. 2019. V. 122. Art. No. 237001.
  15. Niranjan M., Wang Y., Jaswal S.S. et al. // Phys. Rev. Lett. 2009. V. 103. Art. No. 016804.
  16. Niranjan M.K., Burton J.D., Velev J.P. et al. // Appl. Phys. Lett. 2009. V. 95. Art. No. 052501.
  17. Павлов Д.П., Пиянзина И.И., Мухортов В.М. и др. // Письма в ЖЭТФ. 2017. Т. 106. № 7. С. 440.
  18. Tailor N.K., Maity P., Satapathi S. // ACS Photon. 2021. V. 8. P. 2473.
  19. Gustafson J.K., Wines D., Gulian E. et al. // J. Phys. Chem. C. 2021. V. 125. P. 8712.
  20. Grillo A., Faella E., Pelella A. et al. // Adv. Funct. Mater. 2021. V. 31. Art. No. 2105722.
  21. Pavlenko M.A., Tikhonov Y.A., Razumnaya A.G. et al. // Nanomaterials. 2021. V. 12. P. 75.
  22. Hua X., Meng F., Huang Z. et al. // NPJ Quantum Mater. 2022. V. 7. P. 1.

Қосымша файлдар


© Д.П. Павлов, А.О. Чибирев, Т.М. Салихов, Р.Ф. Мамин, 2023